| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 密度 | ASTM D-1505 | 0.947 | g/cm3 | |
| 熔體流動速率 | ASTM D-1238 | 0.75 | g/10min | ||
| 機械性能 | ESCR | ASTM D-1693 | >48 | Hours | |
| 斷裂伸長率 | ASTM D-638 | 600 | % | ||
| 拉伸降伏強度 | ASTM D-638 | 230 | kg/cm2 | ||
| 抗拉伸沖擊強度 | ASTM D-1822 | 260 | kg·cm/cm2 | ||
| 硬度 | ASTM D-2240 | 65 | Shore D | ||
| 拉伸斷裂伸長率 | ASTM D-638 | 250 | kg/cm2 | ||
| 艾氏缺口沖擊強度 | ASTM D-256 | 6 | kg·cm/cm | ||
| 熱性能 | 脆化溫度 | ASTM D-746 | <-70 | ℃ | |
| 軟化點 | ASTM D-1525 | 120 | ℃ | ||
| 熔點 | FPC方法 | 128 | ℃ | ||