鉻剛玉是以氧化鋁為主要原料，適配氧化鉻等。經(jīng)高溫熔煉而成。呈粉紅色、硬度與白剛玉近似，略高于棕剛玉，韌性比白剛玉高。用其制造的磨具，耐用度好，鋒利，自銳性好，磨加工光潔度高，能明顯提高砂輪產(chǎn)品的質(zhì)量。適用于量具，機(jī)床主軸，儀表零件、螺紋工件及樣板磨等精密磨削。
粒度：F24 F30 F36 F46 F54 F60 F70 F80 F90 F100 F120 F150 F180 F220 F240 F280
W50 W40 W28 W20 W14 W10 W7 W5 W3.5 W2.5 W1.5 W1
|
化學(xué)成分 |
|||||
|
成分 |
F12～F80 |
F90～F150 |
F180～F220 |
||
|
低鉻(20PA) |
AL2O3 |
≥98.5% |
≥98.5% |
≥98.0% |
|
|
Cr2O3 |
0.20-0.45% |
0.20-0.45% |
0.20-0.45% |
||
|
NA2O |
≤0.50% |
≤0.55% |
≤0.60% |
||
|
中鉻(45PA) |
AL2O3 |
≥98.2% |
≥98.2% |
≥97.8% |
|
|
Cr2O3 |
0.45-1.0% |
0.45-1.0% |
0.45-1.0% |
||
|
NA2O |
≤0.55% |
≤0.60% |
≤0.70% |
||
|
高鉻(100PA) |
AL2O3 |
≥97.4% |
≥97% |
≥96.5% |
|
|
Cr2O3 |
1.0-2.0% |
1.0-2.0% |
1.0-2.0% |
||
|
NA2O |
≤0.55% |
≤0.60% |
≤0.70% |
||
|
物理性能 |
|||||
|
基本礦物 |
α-Al2O3 |
||||
|
晶體尺寸 |
600-800 μm |
||||
|
莫氏硬度 |
9 |
||||
|
努普硬度 |
2200-2300 kg/cm3 |
||||
|
熔點(diǎn) |
2050 ℃ |
||||
|
比重 |
3.9-4.1g/cm3 |
||||
|
堆積密度 |
1.40-1.91 g/cm3 |
||||
|
顏色 |
粉色 |
||||
|
晶型 |
多棱型 |
||||
鉻剛玉磁性物含量（%）
|
粒度范圍 |
低鉻（20PA） |
中鉻（20PA） |
高鉻（20PA） |
|
F12-F30 |
0.0040 |
0.0050 |
0.0060 |
|
F36-F60 |
0.0036 |
0.0045 |
0.0055 |
|
F70-F120 |
0.0032 |
0.0040 |
0.0050 |
|
F150-F220 |
0.0028 |
0.0036 |
0.0040 |
一般來(lái)說(shuō)，中鉻鉻剛玉廣泛應(yīng)用最為普遍，中鉻鉻剛玉的堆積密度如下：
|
粒度 |
堆積密度（g/cm3） |
|
10目 |
1.75-1.83 |
|
12目 |
1.74-1.82 |
|
14目 |
1.72-1.82 |
|
16目 |
1.71-1.81 |
|
20目 |
1.71-1.80 |
|
22目 |
1.70-1.80 |
|
24目 |
1.69-1.79 |
|
30目 |
1.68-1.79 |
|
36目 |
1.67-1.78 |
|
40目 |
1.68-1.78 |
|
46目 |
1.66-1.75 |
|
54目 |
1.63-1.72 |
|
60目 |
1.61-1.70 |
|
70目 |
1.58-1.68 |
|
80目 |
1.52-1.60 |
|
90目 |
1.50-1.60 |
|
100目 |
1.46-1.58 |
|
120目 |
1.45-1.56 |
|
150目 |
1.45-1.55 |
|
180目 |
1.40-1.51 |
|
220目 |
1.39-1.47 |
用途：
1. 樹(shù)脂砂輪如超薄切割片，打磨片，砂輪有很好的耐用性和鋒利度。
2. 陶瓷砂輪如機(jī)床用磨輪，杯型砂輪，碗型砂輪，磨頭等。
3. 涂附磨具如拋光輪，砂布砂紙，美甲條等。
4. 對(duì)噴砂要求比較高的噴砂操作
5. 精密儀表器件的磨削
6. 工具鋼，不銹鋼，淬火鋼的內(nèi)圓磨，工具磨，仿型磨，成型磨，刀具，量具，螺紋工件，儀表零件等的磨削。
7. 鉻剛玉段砂用于生產(chǎn)高性能耐火磚，定型耐火材料
特性：
氧化鋁純度高，韌性和自銳性好，晶體有多個(gè)鋒利棱角，很好的耐用性能，硬度高，抗沖擊性強(qiáng)，不含鐵元素